Block Copolymers PP granules

Block Copolymers PP granules

Product Details:

X

Product Description

Homopolymer Polypropylene
PP Homopolymer Powder
MFR range-------------------------------------------------------------0.5~100 g/10min (2.16kg)
Stacking Density-------------------------------------------------------------------0.4~0.5 g/m³
Ash Content----------------------------------------------------------------------≤100 mg/kg
Isotacticity------------------------------------------------------------------------------≥97%
Tensile Strength----------------------------------------------------------------------≥30 Mpa
Tensile Elongation at Break-----------------------------------------------------------------≥35%
Flexural Strength---------------------------------------------------------------------≥45 Mpa
Flexural Modulus-------------------------------------------------------------------≥1100 Mpa
IZOD Impact Strength at 23ºC----------------------------------------------------------≥2.5 kJ/m²

Applications:Modification, Injection and Wiredrawing

Detailed Usage including:Monofilament, (Lacerate) Film, Packing Bag, Backing of Carpet, Thread, Rope, Packing Belt, Silk Spinning for Woven Bag, Cast Film or Tube Film, Lamination, The Inner Drum and Base of Washing Machine, Household and Packing or Industry Fiber etc.

Type PP-H-012 PP-H-045 PP-H-075 PP-H-140 PP-H-225- PP-H-225+ PP-H-300- PP-H-300+ PP-H-425- PP-H-425+ PP-H-550
MFR 0.5-2.2 2-6 5-11 10-16 14-19 17-25 24-30 28-35 32-35 42-55 >55
Stacking density 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5 0.4-0.5
Ash content 100 100 100 100 100 100 100 100 100 100 100
Isotacticity 97 95 97 95 97 97 97 97 97 97 97
Tensile strength 30 36 30 35 30 30 30 30 30 30 30
Elongation at break 35 35 35 35 35 35 35 35 35 35 35
Flexural strength 45 45 45 45 45 45 45 45 45 45 45
Flexural Modulus 1300 1300 1300 1300 1100 1100 1100 1100 1100 1100 1100
IZOD Impact Strength 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5


Homopolymer polypropylene is a light density thermoplastic (.91-92gm/cm³).It can be stabilized to enhance prolonged use at elevated temperature, prolonged life in exposure to ultra-violet light and improved flame retardancy.
Homopolymer Polypropylene granules
T30S
Property:
MFR (2.16kg)---------------------------------------------------------------------3~5 g/10min
Isotacticity-----------------------------------------------------------------------------≥95%
Tensile Strenght--------------------------------------------------------------------->30 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Yellow Index-----------------------------------------------------------------------------≤4

Description:A polymer used for general purpose with perfect property in Anti-impact, exhibits excellent processing performance in long-term usage.

Applications:The spinning of woven bag wire, Production of cast film and tube film, Package Material, Carpet, Artificial grass, Rope or mono-silk for packing etc.
 
V30G
Property:
MFR (2.16kg )-------------------------------------------------------------------14~19g/10min
Isotacticity-----------------------------------------------------------------------------≥95%
Tensile Strenght--------------------------------------------------------------------->30 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Notched IZOD Impact Strength at 23ºC----------------------------------------------------≥2 kJ/m²
Flexural Modulus------------------------------------------------------------------>1000 Mpa
Yellow Index-----------------------------------------------------------------------------≤4

Description:High strength, High thermal resistance, Good resistance to flexure, High tensile strength, High inflexibility, High wearability, Good environmental stress crack resistance, Low creep behavior.

Applications:Plastic toys, Containers for packing and Housewares.
 
Z30S
Property:
MFR (2.16kg)-------------------------------------------------------------------26~30 g/10min
Isotacticity-----------------------------------------------------------------------------≥95%
Tensile Strength--------------------------------------------------------------------->30 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Notched IZOD Impact Strength at 23ºC----------------------------------------------------≥2 kJ/m²
Flexural Modulus------------------------------------------------------------------>1000 Mpa
Yellow Index-----------------------------------------------------------------------------≤4

Description:Good fluidity, Narrow molecular weight distribution, Low ash content, Good tensile, High cleanness.

Applications:The fields of high textile rate and high elongation such as carpet or belt material, fibers of sport clothing and heavy clothing.
 
HY9018
Property:
MFR (2.16kg)------------------------------------------------------------------>65 g/10min
Isotacticity-----------------------------------------------------------------------------≥98%
Tensile Strenght--------------------------------------------------------------------->36 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥1.5 kJ/m²
Flexural Modulus------------------------------------------------------------------>1300 Mpa
Yellow Index-----------------------------------------------------------------------------≤4

Description:High flowing rate, High rigidity, Good thermal resistance, Good fineness in surface, Easy forming reapidly.

Applications:DVD packing box, Disposable snack food box, Thin wall product.

Polypropylene can be use in direct contact with food.
 
Random Copolymers
HY-N4200F
Change in the way the material is polymerized can show dramatic improvements in certain mechanical properties, example, random copolymers block copolymers.
Copolymerization of an additional resin group can enhance physical properties.Addition of fillers can improve mechanical or thermal stability.
Property:
Exterior------------------------------------------------------------------------White Powder
MFR-----------------------------------------------------------------0.26~0.3 g/10min, 2.16kg
Ash Content---------------------------------------------------------------------------≤0.03%
Tensile Strength--------------------------------------------------------------------->23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥17 kJ/m²
Flexural Modulus------------------------------------------------------------------->650 Mpa
Melting Point--------------------------------------------------------------------------<146ºC

Description:PP Random Copolymer Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.
 
HY-N4600F
Property:
Exterior------------------------------------------------------------------------White Powder
MFR------------------------------------------------------------------0.3~0.5 g/10min, 2.16kg
Ash Content---------------------------------------------------------------------------≤0.03%
Tensile Strength--------------------------------------------------------------------->23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥17 kJ/m²
Flexural Modulus------------------------------------------------------------------->650 Mpa
Melting Point--------------------------------------------------------------------------<146ºC

Description:PP Random Copolymer, Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.
Resistance to chemicals and solvents is very good.It has good resistance to aqueous salts, acids or alkaline.It also has very low pereability to water vapor and gases.Because of its excellent resistance to solvents, it finds extensive use in the semi-conductor industry.It performs well in the presence of DI water.Care must be taken in the presence of active oxidizing agents, especially with fabricated parts.Mumerous chemical resistance charts are based solely on press molded plaques and don't take fabricated parts into consideration.The resins are attacked however, by halogens, fuming nitric acid and other active oxidizing agents, and by aromatic and chlorinated hydrocarbons at high temperatures.

 
HY-N4200L
Property:
Exterior----------------------------------------------------------------------Natural Granule
MFR-----------------------------------------------------------------0.25~0.28 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥50 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥750 Mpa
Melting Point--------------------------------------------------------------------------<146ºC
Oxidation Induction Time (at 210ºC)-------------------------------------------------------≥30min

Description:PP Random Copolymer, Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.
 
HY-N4600L

Property:
Exterior----------------------------------------------------------------------Natural Granule
MFR------------------------------------------------------------------0.3~0.5 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC----------------------------------------------------≥50kJ/m²
Flexural Modulus--------------------------------------------------------------------≥750 Mpa
Melting Point--------------------------------------------------------------------------<146ºC
Oxidation Induction Time (at 210ºC)-------------------------------------------------------≥30min

Description:PP Random Copolymer, Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.

 It can be processed via extrusion, injection molding, blow molding, compression molding, and rotational molding.It is extremely stable and relatively easy to process.
It is available in various forms such as, but not llimited to, films, sheets, blocks, pipes, hollow tubes, round rods, square rods, profiles, fittings and valves.
Nonstandard shapes are possible through pressure, thermo or vacuum forming.
Great care shoudl be used in designing with polypropylene, taking into consideration its coefficient of thermal expansion, modulus of elasticity, and its compressive strength.
HY-3500TML
Property:
Exterior-------------------------------------------------------------------Transparent Granule
MFR--------------------------------------------------------------------1.5~6 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥29 Mpa
Notched Charpy Impact Strength at 23ºC---------------------------------------------------≥8 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥900 Mpa
Melting Point--------------------------------------------------------------------------<140ºC
Haze Ratio-----------------------------------------------------------------------------<18%
Yellow Index-----------------------------------------------------------------------------≤4

Description:PP random copolymer of high transparency, Perfect transparency and fineness, Good sensory taste, Excellent balance of tenacity and rigidity, High crystallization temperature.

Applications:Widely used for the thermoforming products by technology of 1 or 2 steps method, including high transparent pallet, cups for milk tea or other food containers, furniture product and thin package material, medicine bottle or transparent cup lid by injection, blowing and extrusion method, sheets, stationery product, high transparency and gloss woven bag, and the modification of other polypropylene by blending.
HY-4808TML
Property:
Exterior-------------------------------------------------------------------Transparent Granule
MFR--------------------------------------------------------------------5~12 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥29 Mpa
Notched Charpy Impact Strength at 23ºC---------------------------------------------------≥5 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥900 Mpa
Melting Point--------------------------------------------------------------------------<140ºC
Haze Ratio-----------------------------------------------------------------------------<20%
Yellow Index-----------------------------------------------------------------------------≤4

Description:High transparency random copolymer, low haze ratio.

Applications:Applied to the product of high transparency, The daily transparent necessaries, Medical syringe, Storage box, Transparent lid, sheet and containers.


 
HY-4818TML
Property:
Exterior-------------------------------------------------------------------Transparent Granule
MFR-------------------------------------------------------------------12~20 g/10min, 2.16kg
Tensile Strength----------------------------------------------------------------------≥27Mpa
Notched Charpy Impact Strength at 23ºC---------------------------------------------------≥5 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥900 Mpa
Melting Point--------------------------------------------------------------------------<140ºC
Haze Ratio-----------------------------------------------------------------------------<20%
Yellow Index-----------------------------------------------------------------------------≤4

Description:Random copolymer of high transparency, High resistance to impact, High flowing performance, High speed in forming, Odor free, High gloss, Low haze ratio.

Applications:Suitable to the product requiring a high transparency such as storage container, Disposable syringe, Sports cup, Feeding bottle, Lunch-box, Crisper, Electronic accessories.


KRUNGTHEP TRADING CO.,LTD

* Tips on getting accurate quotes. Please include product name, order quantity, usage, special requests if any in your inquiry.

Listen to the Code(Audio Link)


Back to top
KRUNGTHEP TRADING CO.,LTD. All Rights Reserved.(Terms of Use)
Developed and Managed by Infocom Network Ltd.(Terms of Use)
Developed and Managed by Infocom Network Ltd.